Flexible processing method for metal-insulator-metal capacitor formation

ABSTRACT

A method for forming a metal-insulator-metal (MIM) capacitor includes forming a capacitor bottom plate and a metal interconnect feature on a substrate. A dielectric layer having a predetermined thickness is then formed. The dielectric layer has a first portion overlying the capacitor bottom plate and a second portion overlying the metal interconnect feature. The dielectric layer is processed to adjust the thickness of the first portion of the dielectric layer relative the thickness of the second portion of the dielectric layer. Processing can include etching the first portion of the dielectric layer or adding dielectric material to the second portion of the dielectric layer. A capacitor top plate is formed over the first portion of the dielectric layer to complete the MIM structure.

TECHNICAL FIELD

The present invention relates generally to a semiconductor process method for passive devices, and more particularly to a flexible processing method for Metal-Insulator-Metal (MIM) capacitors.

BACKGROUND

Generally, various Damascene MIM (DA-MIM) capacitor structures are formed within InterMetal Dielectric (IMD) layers. Complicated processes are involved for such formation which include: (1) deposition of an IMD layer for forming within a Capacitor Bottom Metal (CBM) plate, (2) barrier layer deposition, seed layer deposition and bulk metal layer deposition for forming the CBM plate in the IMD layer, (3) deposition of the insulating film for the capacitor dielectric over the CBM plate, (4) barrier layer deposition, seed layer deposition and bulk metal layer deposition for forming a Capacitor Top Metal (CTM) plate over the insulator, and (5) deposition of a via etch stop layer on the CTM plate. One disadvantage of the prior art is that the current DA-MIM process requires several extra masks for formation of the MIM Capacitor. Therefore, it is complicated and costly.

What is needed then is a DA-MIM capacitor formation process and resulting structure that is less costly and complicated than current processes and structures.

SUMMARY OF THE INVENTION

These and other problems are generally solved or circumvented, and technical advantages are generally achieved by preferred embodiments of the present invention, which include a flexible process for forming DA-MIM capacitors.

In accordance with a preferred embodiment of the present invention, the invention provides for a method for forming a metal-insulator-metal (MIM) capacitor. The method includes forming a capacitor bottom plate and a metal interconnect feature on a substrate, and forming a dielectric layer to a predetermined thickness, the dielectric layer having a first portion overlying the capacitor bottom plate and having a second portion overlying the metal interconnect feature. The method also includes processing the dielectric layer to adjust the thickness of the first portion of the dielectric layer relative the thickness of the second portion of the dielectric layer, and forming a capacitor top plate over the first portion of the dielectric layer.

In another aspect, the present invention provides for a method of forming an integrated circuit comprising forming a plurality of circuit elements in a substrate and forming a first metal layer over the substrate, the first metal layer including a capacitor bottom plate and an interconnect feature. The method further includes forming a dielectric layer of substantially uniform thickness over the first metal layer, and adjusting the thickness of the dielectric layer over the capacitor bottom plate, relative the thickness of the dielectric layer over the interconnect feature. The method also includes forming a capacitor top plate over the capacitor bottom plate; and forming an inter-metal dielectric layer over the capacitor top plate and the dielectric layer.

In yet another aspect, the present invention provides for an integrated circuit device. The device includes a capacitor bottom plate formed in a first metal layer and an interconnect feature formed in the first metal layer. The device further includes a continuous dielectric layer formed over the capacitor bottom plate and the interconnect feature, the continuous dielectric layer having a first thickness over the capacitor bottom plate and a second thickness over the interconnect feature. The second thickness is greater than the first thickness. The integrated circuit device also includes a capacitor top plate on the dielectric layer overlying the capacitor bottom plate.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the present invention, and the advantages thereof, reference is now made to the following descriptions taken in conjunction with the accompanying drawings, in which:

FIG. 1 is a cross-sectional view of a first mask stage for an exemplary CBM and inter-connector M7;

FIGS. 2A and 2B are cross-sectional views showing the etching and deposition stage, respectively, for CBM and M7 of the first exemplary embodiment; p FIG. 3 is a cross-sectional view of the deposition stage for an exemplary Via Etch Stop Layer (VESL);

FIG. 4 is a cross-sectional view of a first mask stage for an exemplary CTM;

FIG. 5 is a cross-sectional view of the photo exposition stage for CTM of the first exemplary embodiment;

FIG. 6 is a cross-sectional view of the deposition stage for the exemplary CTM;

FIG. 7 is a cross-sectional view of a second mask stage for the exemplary CTM;

FIG. 8 is a cross-sectional view of the etching stage for the exemplary CTM;

FIGS. 9A through 9C are cross-sectional views of a final assembly of an exemplary MIM capacitor;

FIGS. 10A through 10C are cross-sectional views of intermediate stages of manufacture for a second embodiment of the present invention; and

FIG. 11 is a cross-sectional view of final assembly of the MIM capacitor of the second embodiment of the present invention.

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

The making and using of the presently preferred embodiments are discussed in detail below. It should be appreciated, however, that the present invention provides many applicable inventive concepts that can be embodied in a wide variety of specific contexts. The specific embodiments discussed are merely illustrative of specific ways to make and use the invention, and do not limit the scope of the invention.

The present invention will be described with respect to preferred embodiments in a specific context, namely a semiconductor processing method for forming a DA-MIM capacitor. The invention may also be applied, however, to other DA-MIM components.

FIG. 1 schematically illustrates in cross-section a semiconductor device 10 in an intermediate stage of manufacture. Device 10 includes a substrate 2 in which various active and passive elements (not shown) have been manufactured. Additionally, substrate 2 may include various interconnection layers and interlayer vias, as is well known in the art. In one exemplary embodiment, six interconnection layers (not shown) are formed in substrate 2 and a capacitor bottom plate will be formed in the seventh metal layer, as will be described in detail below. One skilled in the art will recognize that the capacitor structure of the preferred embodiments of the present invention can be formed in other metal layers as a matter of design choice.

As shown, a dielectric layer 4, commonly referred to as an inter-metal dielectric (IMD), is formed over the substrate 2 (i.e., over the underlying devices and layers). IMD 4 is preferably formed of a low k dielectric material such as silicon oxide, silicon nitride, spin-on-glass (“SOG”), TEOS, halogenated SiO, fluorinated silicate glass (“FSG”) or the like, and is preferably deposited by spin-on techniques, electro-chemical plating, chemical vapor deposition (“CVD”), physical vapor deposition (“PVD”), atomic layer deposition (“ALD”), molecular beam epitaxy CVD, and the like. One skilled in the art will recognize that the particular composition of IMD 4 is a matter of design choice. Typically, IMD 4 is deposited to a thickness ranging from 500 to 50,000 (for ultra thick metal) Angstroms. Also shown in FIG. 1 is photoresist layer 6 that has been deposited over IMD 4 and patterned using known photolithographic techniques with an appropriate photolithographic mask for the Capacitor Bottom Metal (CBM) plate. As shown, openings are formed in photoresist layer 6, exposing portions of underlying IMD 4 for forming the CBM. Other metal features are often formed simultaneously as well, such as metal interconnects.

FIG. 2A illustrates the device of FIG. 1 after IMD 4 has been etched in the regions exposed by patterned photoresist layer 6 forming trenches 8 and 9, respectively. Preferably, IMD 4 is anisotropically etched using known etching techniques such as sputter etching, ion-beam etching, plasma etching, and the like, although other techniques could be employed. After the etch step, photoresist layer 6 is removed, again using conventional techniques, such as stripping, ashing and the like.

As shown in FIG. 2B, trenches 8 and 9 are filled with a conductor, preferably copper, using conventional damascene processing techniques. Typically, the trenches are initially lined with a barrier layer/adhesive layer, such as titanium/titanium nitride, or tantalum/tantalum nitride. A copper seed layer is formed over the barrier/adhesive layer(s), after which the trenches are overfilled with a copper layer using electroless plating, electrochemical plating, or the like. The copper layer is then planarized, preferably using a chemical mechanical polish (CMP), as is known in the art.

Illustrated in FIG. 2B are two metal features 12 and 14. As will be explained in greater detail below, feature 12 will serve as the bottom capacitor plate of a preferred embodiment metal-insulator-metal (MIM) capacitor structure. Feature 14 is preferably an interconnect structure by which various passive and active elements (not shown) can be interconnected and/or connected to external components. One skilled in the art will recognize that numerous metal features per metal layer (possibly millions) will likely be simultaneously formed in a typical integrated circuit design.

FIG. 3 illustrates the structure of FIG. 2B after formation of a dielectric layer 16. As will be explained in greater detail below, dielectric layer 16 will serve a dual purpose. A portion of dielectric layer 16 will serve as the dielectric insulating film for the subsequently formed MIM capacitor. Another portion of dielectric layer 16 will serve as a Via Etch Stop Layer (VESL) for subsequent via formation steps. As one skilled in the art will appreciate, it is desirable that the dielectric layer 16 be relatively thin in order to increase the capacitance of the resulting MIM capacitor. On the other hand, it is desirable that the dielectric layer 16 be thick enough to satisfy the functional requirements of an etch stop layer for the subsequently formed via. These two requirements are in conflict.

To overcome this thickness dilemma, in a preferred embodiment of the present invention, dielectric layer 16 is deposited at a thickness that is desirable for the VESL function, over the IMD 4 and metal features 12 and 14. Dielectric layer 16 is preferably formed of a high k dielectric material, such as Al₂O₃, Hfo₂, SiC, SiN, Ta₂O₅, TaON, TiO₂, ZrO₂, or the like. Dielectric layer 16 is preferably deposited by to a thickness of from about 100 Angstroms to about 1000 Angstroms; preferably by CVD or PVD deposition. While a thickness range for preferred embodiments is provided, one skilled in the art will recognize that the appropriate film thickness will depend upon numerous design and performance characteristics.

FIG. 4 illustrates the intermediate device of FIG. 3 after formation of a photoresist 18 that has been formed and patterned atop dielectric layer 16. Note the formation of an opening 19 in photoresist 18, which opening corresponds to the desired size and dimensions of the resulting MIM capacitor.

FIG. 5 illustrates a cross-sectional structure of the device process after dielectric layer 16 has been etched in those regions exposed by photoresist layer 18 (specifically the hole 19 illustrated in FIG. 4, as an example) and photoresist layer 18 has been removed. In a preferred embodiment, dielectric layer 16 is anisotropically etched using, e.g., dry etching for a period of about 30 seconds. Note that capacitor dielectric region 20 of dielectric layer 16 is appreciably thinned as a result of the etch step. Although the desired thickness of capacitor dielectric region 20 will depend upon design choices, in a preferred embodiment, capacitor dielectric region 20 is etched back to a thickness of from about 100 Angstroms to about 500 Angstroms, in order to provided desirable capacitance in the resulting MIM capacitor. Note also that the etch step provides a trench 22 in dielectric layer 16 which can be used to self-align the Capacitor Top Metal (CTM) plate, as described below.

As illustrated in FIG. 6, the CTM is preferably formed by blanket depositing a metal layer 24 over the intermediate structure of FIG. 5. Preferably, metal layer 24 includes a barrier and/or adhesion layer, such as Titanium/Titanium Nitride/Tantalum/Tantalum Nitride formed over dielectric layer 16, including within trench 22, followed by s copper seed layer and finally a bulk copper layer, as is well known in the art. Alternatively, metal layer 24 could be formed of aluminum, gold, silver, platinum, tantalum, titanium, tungsten, and alloys of these metals, or the like. Layer 24 is preferably deposited to a thickness sufficient to overfill trench 22 as illustrated in FIG. 6. Depending upon design choices, the thickness of the metal layer 24 may typically range from a few hundred to a few thousand Angstroms.

As illustrated in FIG. 7, photoresist layer 26 is formed and patterned over the device to cover that portion of metal layer 24 overlying trench 22. In some embodiments, photoresist layer 26 can be formed using the same mask pattern as that used for patterning photoresist layer 18 (see FIG. 4). Layer 24 is then anisotropically etched using known techniques to pattern the layer. The resulting structure, shown in FIG. 8, includes CTM plate 28 aligned over the thin capacitor dielectric region 20 of dielectric layer 16, which further acts as an etch stop layer for subsequently formed vias. Having formed the MIM capacitor structure with a minimum of additional masking steps and cost, the integrated circuit device can be completed using conventional Back End of Line (BEOL) processes.

FIGS. 9A through 9C illustrate an exemplary structure including BEOL components. Specifically, etch stop layer 17 is deposited over the intermediate structure illustrated in FIG. 8, followed by an Anti-Reflective Coating (ARC) layer 21, using conventional materials and deposition processes. These layers are then patterned and removed from the device, except for where the layers overly CTM 28, as shown in FIG. 9B. One skilled in the art will recognize the need for ARC 21 overlying metal feature 28 to assist in subsequent photolithographic steps.

As illustrated in FIG. 9C, dielectric layer 30, etch stop layer 32, and dielectric layer 34 are next formed over the device. The thickness of these layers is not drawn to scale and some of the layers are exaggerated for purposes of illustration only. Layers 30, 32, and 34 preferably are realized as a conventional inter-metal dielectric (IMD) layer, using conventional materials and processes. Next, electrical connection is made to the CBM plate 12, the CTM plate 28, and the other interconnect feature 14, by way of via/trench connections 36, 38, and 40, respectively. These metal features 36, 38, and 40 are preferably formed using well known damascene or dual damascene processes.

An alternative embodiment of the present invention is illustrated in FIGS. 10A through FIG. 11. This alternative embodiment process is identical to the above described process with regards to the steps illustrated in FIGS. 1, 2A and 2B.

FIG. 10A illustrates the intermediate structure illustrated in FIG. 2B, wherein a thin dielectric layer 46 has been deposited. Dielectric layer 46 is preferably formed of silicon carbon and is preferably deposited by CVD. In the illustrated embodiment, dielectric layer 46 is deposited to a thickness of from about 100 Angstroms to about 500 Angstroms—which is a desirable thickness range for achieving preferred capacitance characteristics in the subsequently formed MIM capacitor.

As illustrated in FIG. 10B, CTM 28 is next formed. CTM 28 is preferably formed by convention aluminum processes (blanket deposition, photolithography, etching, as is known in the art).

With reference to FIG. 10C, etch stop layer 17 and ARC 21 are formed over the device and patterned, using materials and processes similar to those described with reference to FIGS. 9A and 9B. This is followed by the formation of a second etch stop layer (ESL) 48, also as illustrated in FIG. 10C. ESL 48 is deposited over layer 46 in those regions not covered by CTM 28. This means that dielectric layer 46 retains its relative thinness in the region of the MIM capacitor, but that dielectric layer 46 and ESL 48 function collectively to form a thicker dielectric layer in those regions where the etch stop functionality is required. Preferably, dielectric layer 46 and ESL 48 have a combined thickness of about 500 Angstroms to about 1000 Angstroms. ESL 48 is preferably formed of the same material using the same deposition processes as dielectric layer 46. As a matter of design choice, other materials may be selected for ESL 48 having different or complimentary properties relative dielectric layer 46.

Having formed the MIM capacitor comprising CBM 12, dielectric layer 46, and CTM 28, processing preferably continues using conventional BEOL processes. FIG. 11 provides one exemplary structure in which IMD layers 30, 32 and 34 are formed over the structure and trench/via structures 36, 38, and 40 are formed to electrically connect to CBM 12, CTM 28, and interconnect feature 14, respectively.

In the preferred embodiment of the present invention only one additional mask for defining CTM 28 is required during the MIM capacitor formation process. CBM plate 12 pattern is defined together with metal feature 14, and hence no extra mask is required for this feature. Flexible thickness control over the via etch stop layer 17 (46/48) and the MIM capacitor insulator is achieved without complicated and costly processes.

Although the present invention and its advantages have been described in detail, it should be understood that various changes, substitutions and alterations can be made herein without departing from the spirit and scope of the invention as defined by the appended claims. Moreover, the scope of the present application is not intended to be limited to the particular embodiments of the processes, materials and steps described in the specification. As one of ordinary skill in the art will readily appreciate from the disclosure of the present invention, processes, materials and steps, presently existing or later to be developed, that perform substantially the same function or achieve substantially the same result as the corresponding embodiments described herein may be utilized according to the present invention. Accordingly, the appended claims are intended to include within their scope such processes, materials and steps. 

1. A method for forming a metal-insulator-metal (MIM) capacitor, comprising: forming a capacitor bottom plate and a metal interconnect feature on a substrate; forming a dielectric layer to a predetermined thickness, the dielectric layer having a first portion overlying the capacitor bottom plate and having a second portion overlying the metal interconnect feature; processing the dielectric layer to adjust the thickness of the first portion of the dielectric layer relative the thickness of the second portion of the dielectric layer; and forming a capacitor top plate over the first portion of the dielectric layer.
 2. The method of claim 1 wherein processing the dielectric layer comprises etching the first portion of the dielectric layer.
 3. The method of claim 1 wherein processing the dielectric layer comprises adding additional dielectric material over the second portion of the dielectric layer.
 4. The method of claim 1 wherein said second portion of the dielectric layer functions as an etch stop layer.
 5. The method of claim 1 further comprising: depositing an inter-metal dielectric layer over the capacitor top plate and the dielectric layer; etching vias in the inter-metal dielectric layer; and filling the vias with a conductor.
 6. A method of forming an integrated circuit comprising: forming a plurality of circuit elements in a substrate; forming a first metal layer over the substrate, the first metal layer including a capacitor bottom plate and an interconnect feature; forming a dielectric layer of substantially uniform thickness over the first metal layer; adjusting the thickness of the dielectric layer over the capacitor bottom plate, relative the thickness of the dielectric layer over the interconnect feature; forming a capacitor top plate over the capacitor bottom plate; and forming an inter-metal dielectric layer over the capacitor top plate and the dielectric layer.
 7. The method of claim 6 wherein the thickness of the dielectric layer is adjusted by etching a portion of the dielectric layer overlying the capacitor bottom plate.
 8. The method of claim 6 wherein the capacitor top plate is formed prior to adjusting the thickness of the dielectric layer and wherein the thickness of the dielectric layer is adjusted by depositing additional dielectric material over the dielectric layer and the capacitor top plate.
 9. The method of claim 6 wherein the dielectric layer is formed having a substantially uniform thickness of from about 100 Angstroms to about 1000 Angstroms.
 10. The method of claim 7 wherein the thickness of the dielectric layer overlying the capacitor bottom plate is adjusted to a thickness of about 100 Angstroms to about 500 Angstroms.
 11. An integrated circuit device comprising: a capacitor bottom plate formed in a first metal layer and an interconnect feature formed in the first metal layer; a continuous dielectric layer formed over the capacitor bottom plate and the interconnect feature, the continuous dielectric layer having a first thickness over the capacitor bottom plate and a second thickness over the interconnect feature, the second thickness being greater than the first thickness; and a capacitor top plate on the dielectric layer overlying the capacitor bottom plate.
 12. The integrated circuit of claim 11 wherein the capacitor bottom plate comprises copper.
 13. The integrated circuit of claim 11 wherein the capacitor top plate comprises a material selected from the group consisting essentially of Al, Ta, TaN, Ti, TiN, and combinations thereof.
 14. The integrated circuit of claim 11 wherein the dielectric layer comprises a material selected from the group consisting essentially of silicon carbide, silicon oxide, silicon nitride, and combinations thereof.
 15. The integrated circuit of claim 11 wherein the first thickness is between about 100 Angstroms and about 500 Angstroms and the second thickness is between about 100 Angstroms and about 500 Angstroms.
 16. The integrated circuit of claim 11 further comprising: a capacitor etch stop layer overlying and substantially aligned with the capacitor top plate; and an anti-reflective coating overlying and substantially aligned with the capacitor etch stop layer.
 17. The integrated circuit of claim 11 wherein the dielectric layer overlying the interconnect feature comprises two layers of dielectric material.
 18. The integrated circuit of claim 17 wherein the two layers of dielectric material have the same composition. 